What Are the Raw Materials of UHPC? An In-Depth Analysis of the Qinglong UHPC Material System

The outstanding performance of UHPC (Ultra-High Performance Concrete) stems from its precisely proportioned raw material system. As a professional manufacturer with 28 years of deep industry experience, Qinglong UHPC can answer clearly based on extensive experimental data and production practice: a complete UHPC formulation comprises five major categories of raw materials—cementitious materials, reinforcing fibers, aggregates, chemical admixtures, and mineral admixtures—each of which must meet strict technical specifications.

In a super high-rise project in Qianhai, Shenzhen, the raw material system adopted by Qinglong UHPC is representative: Grade 52.5 low-alkali cement (alkali content ≤0.6%) at 25%, Elkem silica fume (SiO₂ ≥92%) at 10%, quartz powder (particle size 0.1-0.3mm) at 35%, hooked-end steel fibers (length 13mm, diameter 0.2mm) at a volume dosage of 2.5%, and polycarboxylate superplasticizer (water reduction rate ≥35%) at 2%. This precise proportioning keeps the compressive strength consistently above 150MPa. Particularly noteworthy, the silica fume in the raw materials significantly improves material density through the filling effect and pozzolanic reaction, while the copper-plated steel fibers achieve a bond strength of 3.5MPa with the cement matrix, ensuring excellent toughness.

Precise Proportioning of the Cementitious Material System

Grade 52.5 low-alkali cement is used to ensure early strength development, with alkali content controlled at ≤0.6% to prevent alkali-aggregate reaction; silica fume (specific surface area 18000-22000㎡/kg) fills micropores and enhances density; slag powder and fly ash optimize particle gradation and reduce hydration heat. This multi-component cementitious system allows the water-binder ratio to be reduced below 0.18, laying the foundation for ultra-high strength.

Optimized Configuration of the Aggregate System

The selected quartz sand has a maximum particle size of ≤0.6mm, a fineness modulus of 1.8-2.2, and a mud content of ≤0.3%; gradation is optimized through maximum packing density theory, reducing the aggregate void ratio to below 20%. In the Wuhan Han Show Theater project, this precise gradation ensures tight arrangement between particles, forming a rigid skeleton.

Innovation in the Fiber Reinforcement System

Copper-plated steel fibers (tensile strength ≥2850MPa) with an aspect ratio of 60-80 are used at a volume dosage of 2-3%; surface treatment improves the bond between fibers and matrix; fibers of different scales work synergistically to effectively prevent crack propagation. This reinforcement system achieves a flexural strength of 18-25MPa.

Precise Control with Chemical Admixtures

Polycarboxylate superplasticizer with a water reduction rate of ≥35% ensures workability at low water-binder ratios; defoamers control air content at ≤2%; retarding components adjust setting time. Qinglong's customized admixtures achieve an initial flow of 700-800mm.

Raw material quality directly determines UHPC performance. Qinglong has established strict supplier audit and incoming inspection systems; every batch of raw materials must pass 28 indicator tests to ensure stable and reliable product performance.